CAST STEEL SHOT S460
2015-09-11 13:14:43   From:   Click:

nuoqi shot , CAST STEEL SHOT S460 with Ervin fatigue life 2800 times
\\
 CAST STEEL SHOT S460
一 Performance & Technical standard: 
1. Chemical Composition:
Carbon: 0.8 - 1.2% 
Manganese :0.35-1.2% 
Silicon: ﹥0.4% 
Sulphur : ≤0.05% 
Phosphorus: ≤0.05%
2 Hardness: 
The rate is more than 90% as follows:
Shot:390HV~530HV(40HRC~49HRC)
3 Min Density:
Shot ≥7.2×103kg/m3  Grit≥7.4×103kg/m3
4 Metallurgical Structure: Tempered martensite and small amount of residual austenite and carbide dispersion 
5 Ervin time:
In the same hardness condition: high carbon steel shot fatigue life is about 2800 times
二 The use and application:
1 Blasting cleaning: casting ,die casting, forging , heat treatment, steels ,steel plate , Structural steel 
2 Derusting: casting ,die casting, forging , heat treatment, steels ,steel plate , Structural steel
3 Strenghening: heat treatment ,gears ,shafts, structure steel, ship plate, steels
4 Steel pretreatment :steels ,steel plate ,structure steel ,ship plate ,H style steel.
Application Devices:
Steel shot mainly used for the following equipment including rotary barrel shot blasting machine, chain type shot blasting
 machine,pedrail type shot blasting machine,pass through shot blasting machine,table type shot blasting machine, Pendent
 chain & Pile type Shot Blasting Machine, trolley type shot blasting machine,abrator, abrator equipment,shot peening machine,
shot peening equipment,sandblasting machine,sandblasting equipments,steel material pretreatment production line,steel 
plate pretreatment production line, steel structure pretreatment production line
三 Size: ISO standard (SAEJ-444 Standard)
steel Shot size : S400(S1320)、S300(S1110)、S280(S930)、S240(S780)、S200(S660)、S170(S550)、S140(S460)、S120(S390)、S100(S330)、S080(S280)、S070(S230)、S060(S170)、S040(S110)、S030(S70)

Steel shot :
Steel shot are steel grains made of hypereutectoid alloyed steel by original technology, which allows producing shot with maximum sphericity and provides it with optimal operating properties. We can control the quality and allows receiving the steel shot with stable sieving and best abrasive properties along with high durability. According to the report of independent laboratory the durability of our hihg carbon steel shot exceeds the nominal durability 2700 (+/-50) passes by 10-20 % according to the method Ervin Test, low chrome alloy steel shot exceeds the nominal durability 3400 (+/-50) passes by 10-20 % according to the method Ervin Test, which corresponds 100% to SAE J445 K. Our lab test provides our steel abrasives with excellent abrasive properties due to high rigidity (resilience) of steel shot, which transfers the impact energy on the surface treated, but not on the deformation of abrasive particles. 

Nuoqi steel shot URLhttp://www.nuoqi-steel-shot.com/show-13-86-1.html

Related search:CAST STEEL SHOT S280

The Last:CAST STEEL SHOT S390
The Next: CAST STEEL SHOT S280