alloy steel shot , nuoqi alloy steel shot ,why alloy shot Ervin fatigue life is more longer
alloy steel shot
Generally do not do high-speed steel tensile strength test, and to microstructure, hardness test based.
Tungsten and molybdenum high-speed steel after the proper heat treatment, Rockwell hardness can reach 63 or more, and cobalt-based high-speed steel at 65 or more. Acid leaching of steel low magnification there is no visible shrinkage, turning the skin. Center porosity, generally less than one loose.
Metallographic examination of the contents include carbon layer, microstructure and carbide of three projects.
1. High speed steel should not have a significant decarbonization. Microstructure not have herringbone eutectic ledeburite exist.
2. High-speed steel carbide of the greatest impact on the quality, metallurgy and machinery sector level carbide of very great importance. It may propose carbide of different level requirements according to different uses of steel, usually less than three.
3. The high-speed steel cutting tools, in addition to its high hardness, high wear resistance and toughness enough, there is one important factor is having red hardness. (Red hardness refers to the tool at high cutting edge capability softening resistance in the red-hot state.)
One measure is to put red hardness of steel is heated to 580 ~ 650 ℃, heat 1 hour, then cooled, so that repeated four times to measure the hardness value. High-speed steel quenching temperature near the melting point of steel generally, such as tungsten high speed steel is 1210 ~ 1240 ℃, high molybdenum high-speed steels of 1180 ~ 1210 ℃. After quenching normally takes between 540 ~ 560 ℃ tempering three times. Quenching temperature can be increased to improve the red hardness of steel. In order to improve the life of high-speed steel cutting tools, can be enhanced treatment of their surface, such as low temperature cyanide, nitrogen, sulfur and nitrogen permeation and the like.